Abstract

Single crystals of EuPd$_3$Si$_2$ were grown using a high-temperature EuPd-flux method. The material was structurally and chemically characterized by single-crystal x-ray diffraction, powder x-ray diffraction, Laue method and energy-dispersive x-ray spectroscopy. The structural analysis confirmed the orthorhombic crystal structure (space group $Imma$) but revealed differences in the lattice parameters and bond distances in comparison to previous work by Sharma et al.. The composition is close to the ideal 1:3:2 stoichiometry with an occupation of 7 % of the Si sites by Pd. The heat capacity, electrical resistivity, and magnetic susceptibility show two magnetic transitions indicating antiferromagnetic ordering below $T_{\rm N1}= 61\,\rm K$ and a spin reorientation at $T_{\rm N2}= 40\,\rm K$. The orthorhombic material shows magnetic anisotropy with field applied along the three main symmetry axes, which is summarized in the temperature-field phase diagrams. The susceptibility data hint to an alignment of the magnetic moments along $[100]$ between $T_{\rm N1}$ and $T_{\rm N2}$. Below $T_{\rm N2}$ the magnetic structure changes to an arrangement with moments canted away from $[100]$. In contrast to published work by Sharma et al., the single crystals investigated in this study show AFM order below $T_{\rm N1}$ instead of ferromagnetism that sets in at higher $T_{\rm C1}=78\,\rm K$ which might originate from certain differences in the structure, composition or defects that have an impact on the dominant coupling constants of the RKKY interaction.